Synthesis and characterization of carbon nanofilms for chemical sensing
Item
-
Title
-
Synthesis and characterization of carbon nanofilms for chemical sensing
-
Identifier
-
d_2009_2013:83e8c5d7b712:11481
-
identifier
-
11933
-
Creator
-
Kumar, Vivek,
-
Contributor
-
Alexander M. Zaitsev
-
Date
-
2012
-
Language
-
English
-
Publisher
-
City University of New York.
-
Subject
-
Inorganic chemistry | Materials science | Chemical sensors
-
Abstract
-
Carbon nanofilms obtained by high temperature graphitization of diamond surface in inert atmospheres or vacuum are modified by treatment in plasma of different precursor gases. At temperatures above 1000 °C, a stable conductive film of thickness between 10 - 100 nm and specific resistivity 10-3--10-4 Om, depending upon the heating conditions and the growth atmosphere, is formed on diamond surface. A gray, thin film of high surface resistivity is obtained in high vacuum, while at low vacuum (below 10-4 mbar), a thick black film of low surface resistivity forms. It is observed that the exposure to plasma reduces the surface conductance of carbon nanofilms as result of a partial removal of carbon and the plasma-stimulated amorphization. The rate of the reduction of conductance and hence the etching ability of plasma depends on the type of precursor gas. Hydrogen reveals the strongest etching ability, followed by oxygen and argon, whereas SF6 is ineffective. The carbon nanofilms show significant sensitivity of their electrical conductance to temperature and exposure to the vapors of common organic compounds. The oxygen plasma treated films exhibit selective response to acetone and water vapors. The fast response and recovery of the conductance are the features of the carbon nanofilms. The plasma-treated carbon nanofilm on graphitized diamond surface is discussed as a promising sensing material for development of all-carbon chemical sensors, which may be suitable for biological and medical applications.;An alternative approach of fabrication of temperature and chemical sensitive carbon nanofilms on insulating substrates is proposed. The films are obtained by direct deposition of sputtered carbon on highly polished quartz substrates followed by subsequent annealing at temperatures above 400 °C. It is observed that the as-deposited films are essentially amorphous, while the heating induces irreversible structural ordering and gradual conversion of amorphous carbon in disordered graphite. This evolution is confirmed by Raman spectroscopy and electrical measurements.;The carbon nanofilms grown on diamond and deposited on quartz both show similar exponential dependence of their conductance on temperature, which is essentially different from the usual behavior of the thermally activated conduction and the conduction due to variable range hopping of charge carriers. The observed exponential dependence of conductance is explained by a model based on the thermally vibrating energy barriers.;The as-grown nanofilms on diamond surface show a negative response (decrease in conductance) to the vapors of acetone, toluene and hexane, and a positive response (increase in conductance) to the water vapor. Sensitivity (relative change in conductance) to toluene is greater than to water, acetone, and hexane, in that order. Plasma exposure alters the sensitivity to positive for all the organic vapors. Overall, an increase in sensitivity is observed with the plasma exposure time. For acetone and water, an increased exponential dependence on vapor concentration is also observed. The exposure to oxygen plasma renders the carbon films on diamond selectively sensitive to acetone and water vapors. The hydrogen plasma exposure makes the films selectively sensitive to toluene vapor. It is found that the carbon nanofilms on quartz have p-type conductivity, as indicated by the opposite response to NO2 and NH3 analytes. NO2, a known electron acceptor, increases the conductance. NH3, a known electron donor, decreases the conductance. The phenomenological description of the chemical sensitivity of the carbon nanofilms sigma = beta/tau is proposed as a function of two main parameters: the time constant tau and the maximum relative change in conductance beta. tau and beta are described as the parameters related to the surface and bulk material properties of the films, respectively.
-
Type
-
dissertation
-
Source
-
2009_2013.csv
-
degree
-
Ph.D.
-
Program
-
Chemistry